HigrafTSSTERMOGRAF MSS316  can be combined with various interlayer materials to improve performance and handling. Carbon Steel Tanged Metal, Aluminum and SS316L/SS304, Nickel foil are available.
  •  FGS is pure graphite sheet without insertment
  •  ASS316 is graphite sheet reinforced by adhesive 0.05MM SS316 insert.
  •  ASS304 is graphite sheet reinforced by adhesive 0.05MM SS304insert.
  •  TSS316 is graphite sheet reinforced by tanged 0.1MM SS316 insert
  •  TTSS is three layer graphite sheets reinforced by two layers of tanged SS
  •  TSS304 is graphite sheet reinforced by tanged 0.1MM SS304 insert
  •  TCS is graphite sheet reinforced by tanged 0.2-0.25MM carbon steel
  •  MSS316 is graphite sheet reinforced by 24 mesh wire SS316 insert
  •  MSS304 is graphite sheet reinforced by 24 mesh wire SS304 insert
  •  AGN is graphite sheet reinforced by adhesive nickel foil insert

Specification:

Density 0.7-1.6g/cm3
Thickness 0.5MM-6.0MM
Size 1000MM X 1000MM; 1500MM X 1500MM;

1000MM X 2000MM; 1500MM X 2000MM

1500MM X 3000MM; 1000MM X 3000MM

610MM X 610MM; 1270MM X 1270MM

Technical Data

Maximum Operating Temperature1 450 ?aC
Compressibility ASTM F36A 33 – 38 %
Recovery ASTM F36A (min) 13 – 18 %
Flexealing hot compression test 50 MPa 300?aC
Thickness decrease 23?aC 40 %
Thickness decrease 300?aC 1.5 %
Gas leakage DIN 3535/6 <0.8 ml/min
Stress Relaxation DIN 52913 (16h, 300?aC) 48 MPa
Thickness increase ASTM F146
ASTM Oil No. 3 (5h/150?aC) 5 – 10 %
ASTM Fuel B (5h/23?aC) 4 – 6 %
Ethylene glycol/water (1:1) (5h/150?aC) 3 – 5 %
Density (Standard) 1.0 g/cm2
Chloride Content (graphite layer) max 40 ppm
Maximum allow. surface stress @ 450?aC 150 MPa
Graphite Purity min 98 %

Note: